Ask Lemmy
A Fediverse community for open-ended, thought provoking questions
Please don't post about US Politics. If you need to do this, try [email protected]
Rules: (interactive)
1) Be nice and; have fun
Doxxing, trolling, sealioning, racism, and toxicity are not welcomed in AskLemmy. Remember what your mother said: if you can't say something nice, don't say anything at all. In addition, the site-wide Lemmy.world terms of service also apply here. Please familiarize yourself with them
2) All posts must end with a '?'
This is sort of like Jeopardy. Please phrase all post titles in the form of a proper question ending with ?
3) No spam
Please do not flood the community with nonsense. Actual suspected spammers will be banned on site. No astroturfing.
4) NSFW is okay, within reason
Just remember to tag posts with either a content warning or a [NSFW] tag. Overtly sexual posts are not allowed, please direct them to either [email protected] or [email protected].
NSFW comments should be restricted to posts tagged [NSFW].
5) This is not a support community.
It is not a place for 'how do I?', type questions.
If you have any questions regarding the site itself or would like to report a community, please direct them to Lemmy.world Support or email [email protected]. For other questions check our partnered communities list, or use the search function.
Reminder: The terms of service apply here too.
Partnered Communities:
Logo design credit goes to: tubbadu
view the rest of the comments
I'm a sword guy. I spent over a decade training in historical swordsmanship (mostly European longsword - a mix of Fiore and Lichtenaur; but also a little kenjutsu).
There are so many bad takes about swords out there, but I think my personal "favorites" are about the folded steel technique used to forge katana.
See, to make a good sword, you need good steel which is iron + carbon. More carbon = harder steel. Harder steel is better for holding an edge, but also less flexible and more likely to shatter. All swords, European, Japanese or otherwise had to balance those concerns.
Anyway, in Japan, their katana forging technique used steel with slightly differing carbon amounts wrapped in layers in the blade. This layering had a couple of important metallurgical effects:
It gave the core steel a more consistent quality. Since the method they had of producing steel contained varying levels of carbon, the repeated layering, folding, heating and hammering evened it out.
The layering also increased the strength of the steel. By adding layers of high and low carbon steel, the sword smiths could control the flexibility vs strength of the core.
Ok, so without getting too deep in the weeds, that's (basically speaking) why katana were made of folded steel.
But I have been "informed" by so many people that folded steel:
In summary: katana are great - but not magic! The folded steel technique enabled forging swords of high-quality, consistent steel at a time when that was really hard to do. But that's it.
/self looks at rant
Uh... Thank you for coming to my TED Talk.
Yes, hello. I'd like to subscribe to swordfacts
Fact: Swords are easy - the pointy bit goes in the other guy.
I call those greetstabs
Hi! This is my greetsword!
Swordfish can swim at speeds of over 3mph.
Come back tomorrow for more sword facts!
The funny part is when you remind the weebs how bad the iron commonly found in Japan was just not great quality and purity which they lacked the know how to correct, so the folding technique was developed to make their steel workable. If European techniques had been used on Japanese Steel, you'd have one very shoddy sword.
I was under the impression the folding technique of Japanese blades was due to the low carbon content and the process of folding included adding carbon to the iron as well as incorporating it throughout the metal.
European iron ore already had larger amounts of carbon which meant the folding and adding carbon process wasn't required to create a serviceable edge.
It's a little bit of both.
Iirc, Japanese iron was usually in sand form, gathered, rather than mined. So the raw material was smaller and contained less natural carbon than mined ore.
(Though nobody had near the advantage of Indian steel from the Damasc region - Damascus steel naturally had more carbon in their iron and it made for very high quality steel at the time.)
Anyway, at that time Europe had similar techniques for making iron into steel and normalizing the carbon. They would use more resource-intensive techniques, like stacking rods of wrought iron in a furnace with charcoal, then working the carbon-infused rods to distribute the carbon evenly.
That works great when you have access to millions of square miles of forest (for charcoal) and loads of iron ore.
But it's not really about whose steel was "the best", it's just that the "folding" technique was a metallurgical process and had no impact on the quality of the sword (except insofar as it was turning iron into steel).
Oh for sure on all points.
I was just saying that the intensive folding process wasn't nearly as necessary for the euro smiths. Especially, as you said, they had more than enough carbon sources to make up for any deficits in their iron sources.
Once the smith turns the raw material into steel, there was very little difference beyond what the final product needed in hardness/flexibility.
Sword Guy, embrace that. TED Talk away, everytime swords are even slightly relevant.